The role of Si impurities in the transient dopant segregation and precipitation in yttrium-doped alumina

Official URL: http://dx.doi.org/10.3139/146.110258

Y-doped alumina was sintered at 1500 degrees C for 10 h under ultra-clean experimental conditions without experiencing any abnormal grain growth. The yttrium was fairly homogeneously distributed at the grain boundaries, with a mean value of (Gamma) over bar (Y) = 5.5 at nm(-2). The Y-Al-O precipitates in the clean, Y2O3-doped alumina specimen were the YAP (YAlO3) phase, whereas only the YAG (Y3Al5O12) phase was present in the Y2O3-doped alumina samples contaminated with SiO2. The excess concentrations of Y and Si atoms at the grain boundaries that, at the same time, provoke the formation of structurally complex YAG precipitates and abnormal grain growth were both estimated to be at 4-5 at nm(-2). The compositions of the triple point pocket phases found in the region of the exaggeratedly grown alumina grains indicate the presence of alumino-silicate bulk liquids at the sintering temperature.