Influence of SiC addition on tribological properties of SiAlON

Warning The system is temporarily closed to updates for reporting purpose.

Mallik, Awadesh Kumar and Reddy, K. Madhav and Açıkbaş, Nurcan Çalış and Kara, Ferhat and Mandal, Hasan and Basu, Debabrata and Basu, Bikramjit (2011) Influence of SiC addition on tribological properties of SiAlON. Ceramics International, 37 (7). pp. 2495-2504. ISSN 0272-8842

Full text not available from this repository.

Official URL: http://dx.doi.org/10.1016/j.ceramint.2011.03.055


The tribological properties of gas pressure sintered SiAlON and its composite with 18 wt% silicon carbide (SiC) against two different mating materials, i.e., alumina and SiAlON are evaluated. SiAlON and SiAlON-18%SiC composite ceramics were prepared by pressure less sintering and gas pressure sintering. Fretting wear tests were carried out under dry unlubricated ambient conditions (room temperature 23-25 degrees C; relative humidity 50-55%) with a load of 8 N for 45,000 cycles. Friction and wear properties of SiAlON-SiC proved better than the monolithic SiAlON. The formation of silica roll like structure on the composite worn surface was observed.

Item Type:Article
Uncontrolled Keywords:Sintering; SiAlON and SiAlON-SiC composite; Hertzian contact pressures; Silica roll; Tribology
Subjects:T Technology > TA Engineering (General). Civil engineering (General) > TA401-492 Materials of engineering and construction. Mechanics of materials
T Technology > TP Chemical technology > TP0785-869 Clay industries. Ceramics. Glass
ID Code:17322
Deposited By:Hasan Mandal
Deposited On:28 Oct 2011 10:09
Last Modified:30 Jul 2019 14:20

Repository Staff Only: item control page