Preparation and characterization of phosphine oxide based polyurethane/silica nanocomposite via non-isocyanate route
Hoşgör, Zuhal and Kayaman-Apohan, Nilhan and Karataş, Sevim and Menceloğlu, Yusuf Z. and Güngör, Atilla (2010) Preparation and characterization of phosphine oxide based polyurethane/silica nanocomposite via non-isocyanate route. Progress in Organic Coatings, 69 (4). pp. 366-375. ISSN 0300-9440
Official URL: http://dx.doi.org/10.1016/j.porgcoat.2010.07.010
A novel carbonate-modified bis(4-glycidyloxy phenyl) phenyl phosphine oxide (CBGPPO) was synthe- sized to prepare phosphine oxide based polyurethane/silica nanocomposites. Spherical silica particles were prepared according to Stöber method and modified with cyclic carbonate functional silane coupling agent (CPS) to improve the compatibility of silica particles and organic phase. The cyclic carbonate- modified epoxy resins and silica particles were used to prepare hybrid coatings using hexamethylene diamine as a curing agent. The cupping, impact and gloss measurements were performed on aluminum panels, and the tensile test, gel content, thermal and morphological analyses were conducted on the free films. No damage was observed in the impact strength of the coatings. Incorporation of silica and CBGPPO into formulations increased modulus and hardness of the coating making the material more brittle. It was also observed that, the thermal stability of hybrid coatings enhanced with the addition of silica and CBGPPO.
Repository Staff Only: item control page