Structural characterization of semicokes produced from the pyrolysis of petroleum pitches

Warning The system is temporarily closed to updates for reporting purpose.

Okyay, Firuze and Yürüm, Alp and Yürüm, Yuda (2015) Structural characterization of semicokes produced from the pyrolysis of petroleum pitches. Journal of Analytical and Applied Pyrolysis, 111 . pp. 15-26. ISSN 0165-2370 (Print) 1873-250X (Online)

This is the latest version of this item.

[thumbnail of This is a RoMEO green journal -- author can archive pre-print (ie pre-refereeing)] PDF (This is a RoMEO green journal -- author can archive pre-print (ie pre-refereeing))
JAAP-D-14-00422.pdf

Download (2MB)

Abstract

Semicokes obtained from the pyrolysis of petroleum pitches are important materials that are used in the manufacture of many carbonaceous products. Therefore, new structural information of the semi-cokes will extend their utilization. The structural analysis of anisotropic semicokes of the pyrolysis of petroleum pitches obtained under various experimental conditions of temperature and time was investigated. The overall objective is to provide further detailed information of factors which influence formation of anisotropy or turbostratic structures in resultant semicokes. Experiments were carried out under an argon atmosphere at the temperature range of 500-1000 degrees C for 30, 60 and 120 min in a tube furnace. FTIR, H-1-NMR, and C-13 NMR results showed that the aromatic structure of the semicokes was increasing with respect to increasing temperature as well as increasing time. Aromaticity of the semicokes was calculated as 0.54 and 0.64, for Pitch A at 500 degrees C after 120 min, and Pitch B at 600 degrees C after 120 min, respectively. The intensity ratio between Raman "D" and "G" peaks, I-D/I-G (commonly used to characterize disorder in graphene structures) was observed to increase approximately linearly from 0.65 to 0.92 when the pyrolysis temperature of Pitch A was increased from 500 degrees C to 900 degrees C. XRD patterns of the semicokes showed the formation of some crystalline material with time and temperature. The average number of layers, calculated by the Debye-Scherer technique using the XRD patterns of the semicokes, was between 5 and 10. SEM images of the semicokes indicated the presence of turbostratic structures. All the results of characterizations were consistent and indicated the formation of highly amorphous hydrocarbon materials that contain turbostratic structures. Treatments at higher temperatures increased formations of aromatic structure with increased crystallinity. Temperature seemed to be the dominating parameter of the pyrolysis reactions. As the pyrolysis temperature was increased, aromatic structure formation was favored with increased crystallinity in the semicokes. We expect that findings of the present work will open new uses for the anisotropic semicokes obtained from petroleum pitches. The pitches can be widely applied to the templating synthesis of carbon nanostructures and other carbon nanomaterials.
Item Type: Article
Uncontrolled Keywords: Pyrolysis; Petroleum pitches; Semicoke; Turbostratic structure; Aromaticity
Subjects: T Technology > TP Chemical technology
T Technology > TP Chemical technology > TP0315-360 Fuel
Divisions: Sabancı University Nanotechnology Research and Application Center
Faculty of Engineering and Natural Sciences > Academic programs > Materials Science & Eng.
Faculty of Engineering and Natural Sciences > Basic Sciences > Chemistry
Faculty of Engineering and Natural Sciences
Depositing User: Yuda Yürüm
Date Deposited: 05 Jan 2015 10:55
Last Modified: 26 Apr 2022 09:21
URI: https://research.sabanciuniv.edu/id/eprint/26644

Available Versions of this Item

Actions (login required)

View Item
View Item