Effect of gamma-irradiation on the structure of activated carbons produced from Turkish Elbistan lignite
Erçin, Demet and Eken, Mahmut and Aktaş, Zeki and Çetinkaya, Sevil and Sakintuna, Billur and Yürüm, Yuda (2005) Effect of gamma-irradiation on the structure of activated carbons produced from Turkish Elbistan lignite. Radiation Physics and Chemistry, 73 (5). pp. 263-271. ISSN 0969-806X
This is the latest version of this item.
Official URL: http://dx.doi.org/10.1016/j.radphyschem.2004.09.025
The results of the treatment of activated carbons prepared from Turkish Elbistan lignite with γ-irradiation from a 60Co source are presented and associated volatilization of surface material of the activated carbon as a means to obtain a physical modification of the material is discussed in terms of changes in surface area, free radical concentrations and structural changes determined with FTIR and solid-state 13C NMR spectroscopical methods. BET areas of irradiated samples are measured to be greater than those of non-irradiated samples; this might be considered as an indication to some loss of material from the surface by γ-irradiation. γ-Irradiation caused remarkable erosion on the surface with the loss of some carbonaceous matter by probable bond cleavage reactions. As the activation temperature was raised, both of the carbon content and the intensities of the carbon functionalities decreased in the 13C NMR spectra. The observation of symmetric shapes in the ESR spectra might be considered as an indication to the delocalization of the electrons over the graphite-like microcrystallites present in the active carbons. The broadening of the ESR signals in the present work might be both due to the effect of oxygen during the measurements in lower activation temperatures and the enhanced effect of the presence of Fe3+ ion in the form of pyrites in the mineral matter the lignite used. Increase of the relative intensities of free radicals with activation temperature may be indicative of some molecular cracking leading to organic radicals. Irradiation of the activated carbon samples seemed to increase the peak widths and g-values. g-value of 2.003 was due to semiquinone-type free radical which was probably created in oxidation reaction during activation processes.
Available Versions of this Item
Repository Staff Only: item control page