Solid oxide carbonate composite fuel cells: size effect on percolation

Shawuti, Shalima and Gülgün, Mehmet Ali (2016) Solid oxide carbonate composite fuel cells: size effect on percolation. (Accepted/In Press)

[img]PDF - Registered users only - Requires a PDF viewer such as GSview, Xpdf or Adobe Acrobat Reader
1687Kb

Official URL: http://dx.doi.org/10.1016/j.ijhydene.2016.07.208

Abstract

In the studies of solid oxide carbonate composite fuel cell, percolation behaviour of the two phases was investigated as a function of particle size of the oxide phase. The ratio of amount of samarium doped ceria (SDC; Sm0.2Ce0.8O) to Na2CO3 was varied to determine an optimum ionic conductivity as function of oxide particle size. The roles of both phases in the composite electrolyte were investigated. SDC particles were mixed in different amounts of Na2CO3 to obtain composites with carbonate ratios from 1 wt% to 50 wt%. Micro-structural investigations showed that Na2CO3 phase served as the matrix in the micro-structure gluing the oxide particles together. The lowest and the highest carbonate ratios caused low conductivities in the composite as in these samples the 3D connectivity of both phases were disrupted. Low conductivity at both ends of the mixture composition could be interpreted as none of the components of the composite dominated the ionic conductivity. The highest conductivity was obtained at 10 wt% Na2CO3 amount in the composite electrolyte when nano-sized SDC (5e10 nm) oxide powders were used. Two different particle sizes of SDC powders were used to show that the optimum phase ratio, i.e. percolation of both phases, is function of particle size as well. The conductivity in the composite showed percolation behaviour with respect to the two constituent phases.

Item Type:Article
Subjects:UNSPECIFIED
ID Code:30710
Deposited By:Shalima Shawuti
Deposited On:06 Nov 2016 15:56
Last Modified:06 Nov 2016 15:56

Repository Staff Only: item control page